Neoprene Compound
Properties of neoprene compound used to manufacture elastomeric bearings.PHYSICAL PROPERTIES - AASHTO M251-92
TABLE 1 | | PROPERTIES | ASTM STANDARDS | RESULTS | | Tensile Strength (PSI/Mpa) | D412 | >2250PSI/156Kg/cm2 | | Elongation at break % | D412 | >350 | | Hardness (Shore A) | D2240 | 60 (± 5) | | Compressive set % | D395 | 35 | | Bond Strenght kN/m | D429 A | 7.1 kN/m (± .05) | | Peel Strength | D429 B | 7.1 kN/m(± .05) | | AGED FOR 70 HRS AT 100° C as per ASTM D573 | | Tensile Strength (PSI/Mpa) | . | -15% | | Elongation At Break % | . | -40% | | Hardness (Shore A) | . | +15% |
Physical properties of Natural Rubber Compound will be as per BS 5400 with shore A 60 hardness. Click to visit AASHTO M 251 Specifications for Elastomeric bearings and use the back key on your browser to return back to this site. The above given properties are results obtained on random sample testing carried out at laboratory conditions.
|